CP 394 0,8L Grey

Epoxy primer 2K HS 1:1

CP 394 primer is an advanced product that provides excellent corrosion protection for steel surfaces thanks to high-quality resins and active additives. Its outstanding properties make it an ideal choice for industrial and automotive applications where the highest quality and durability are required.

Thanks to specially selected ingredients, CP 394 effectively protects steel from corrosion, providing long-lasting protection even in harsh conditions. The primer adheres well to a variety of substrates such as steel, galvanized steel, aluminum, GRP (fiberglass) and old paint finishes.

CP 394 is a strongly opaque primer that perfectly masks imperfections in the surface, preparing it for further stages of painting. The product can be used both wet-in-wet and as a filler primer to suit different needs and application conditions.

The product is available in a 0.8-liter spill, making it a convenient solution for smaller projects or touch-ups. CP 394 in gray is an indispensable part of any workshop, guaranteeing not only an aesthetically pleasing, but above all durable and professional surface finish. Thanks to its versatility and excellent protective properties, it is the number one choice for professionals who value quality and reliability.

back to main product

Product benefits: Very good adhesion Wet-on-wet application Corrosion protection Insulating properties Superb coat tightness

Compare

more information on this product

Specification

Application

Specification

VERY GOOD ADHESION

INSULATING PROPERTIES

WET-ON-WET APPLICATION

CORROSION PROTECTION

SUPERB COAT TIGHTNESS

WET-ON-WET

One coat, next coat application,
film thickness 20-30 μm

SPRAY VISCOSITY

16-22 sec. DIN Flow Cup 4 mm

RECOMMENDED SIZES FOR PAINT STRAINER

190 μm (wet-on-wet 125 μm)

PAINT EFFICIENCY

8-10 m2/l

POT LIFE

1 hrs

DRY FILM THICKNESS

- 1 coat - 20-40 μm
- 2 coats - 40-80 μm

WET SANDING

P600->P800->P1000

DRY SANDING

P280->P400

MINIMUM SHELF LIFE

CP 394: 24 months in originally
sealed packaging
CP 294: 12 months in originally
sealed packaging

VOC

2004/42/WE IIB(c) (540) 540

Application

SUBSTRATE PREPARATION

Abrade substrate using a red P300-400 abrasive pad by hand for steel,
galvanised steel or grey abrasive pad for aluminium. Alternatively, P180-P240
sanding disc using orbital sander. Remove dust particles before cleaning substrate
with CP 015. After the substrate is clean and dry apply CP 394 with the required
number of layers, taking note of the recommended evaporation time between
coats. Bake or airdry before progressing to the next step of the process

MIXING RATIO

1:1
100 parts of CP 394
100 parts of CP 294 hardener
The wet-on-wet method requires
10-30% of thinner
CP 040/ CP 070/ CP 055/ CP 075

SPRAY GUN SETTINGS

Nozzle 1.6-1.8 mm;
Operating pressure: HVLP/RP 1.8-2.0 bar
Wet-on-wet method:
Nozzle size HVLP/RP 1.3-1.4 mm;
Operating pressure: 1.8-2.0 bar

APPLICATION

2 full coats (filling primer)
1 full coat including 10-30% thinner
(insulator)

EVAPORATION TIME AFTER APPLICATION

5-10 min. after priming at
20°C and 65% relative humidity
Evaporation continues until a matt
surface is visible

DRYING

Drying times at 20°C and
65% relative humidity:
- dust dryness: 10 min (2 coats)
- before sanding: 3 hrs
Drying times at 60°C and
65% relative humidity:
- before sanding 30 min